Micro-cracking process in TBCs (Thermal Barrier Coatings) due to thermal exposure was investigated using SEM (Scanning Electron Microscope) and EBSD (Electron BackScatter Diffraction) observation. Splat particle morphologies in TBCs were clearly visualized by IPF (Inverse Pole Figure) mapping. The splat structure of top coat was consisted with large granular particle region and cluster of small columnar particle region. Cracks were observed along the interfaces of large granular particle region and the cluster of small columnar particle region, along the interfaces among large granular particles and across the cluster of small columnar particles transgranularly perpendicular to columnar crystal growth direction. The onset time of extensive macro crack formation was corresponding to the Cr oxide growth at TGO (Thermally Grown Oxide) to some extent. Thus EBSD observation can be used as a powerful tool for crystallographic observation of TBC, associated with SEM and optical microscope observation.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 76 (767), 812-817, 2010
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679455545728
-
- NII論文ID
- 110007685179
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 10783764
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可