形状記憶合金アクチュエータによる積層複合材料の層間はく離き裂進展の抑止

DOI Web Site Web Site 参考文献15件

書誌事項

タイトル別名
  • Suppression of Delamination Crack Propagation in Laminated Composites by Using Thin SMA Plates
  • ケイジョウ キオク ゴウキン アクチュエータ ニ ヨル セキソウ フクゴウ ザイリョウ ノ ソウ カン ハクリ キレツ シンテン ノ ヨクシ

この論文をさがす

説明

The use of thin actuator plates bonded to surfaces of laminated composites to suppress the growth of delamination cracks is investigated. A composite beam analysis was performed to estimate the effect of actuation strains on the strain energy release rate of delamination cracks. When compared at the same value of actuation strain, the increase in the apparent crack growth resistance is larger for smaller FRP thickness and for smaller value of the critical strain energy release rate of FRP without actuators, Gcr, under both mode I and II loadings. Mode I delamination suppression tests of unidirectional CFRP laminates were conducted by using thin SMA actuators. The value of the apparent crack growth resistance, Glapp, under actuation strains of about 0.1% was 2.5 times larger than fracture toughness of CFRP and was also about 1.5 times as large as that just before actuation.

収録刊行物

参考文献 (15)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ