ぜい性プラスチック板材の切欠き破壊強度と破面模様の関係　　き裂内負荷様式の場合

DOI Web Site Web Site

書誌事項

タイトル別名
  • Relationship between sharply notched fracture strength and fracture surface marks in a brittle plastic in tension. (In the case of an inside loading)
  • ゼイセイ プラスチック イタザイ ノ キリカキ ハカイ キョウド ト ハメン

この論文をさがす

抄録

The fracture strength was varied by changing an inter-grip distance (which we call a gage length here) of a sharply center-notched tensile sheet specimen of unsaturated polyester resin, where the specimen width, thickness, crack length and loading method were kept constant. The loading method is such that the main load works on a central-line parallel to the axis of loading which crosses perpendicularly the central crack length. We call this an inside loading in contrast to an outside loading (1). The number, density, area ratio of fracture surface marks vary with the fracture strength of the material. The total number of marks increases with the fracture strength. The density and area ratio marks increase at each different rate with respect to fracture strength. These results are discussed with the analytical relations of the fracture strength, the dynamic stress-intensity factor and the dynamic strain-energy-release rate by employing the reported relations. The fracture surface marks are examined by the two-dimensional equation of fracture surface marks, and the analytical area ratio of the marks is also calculated.

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ