- The distribution of residual stresses of S 55 C quenched by aqueous polymer solutions.
- スイヨウセイ ポリマー ヤキイレエキ ニ ヨル S55C ノ ヤキイレ ザンリ
この論文をさがす
抄録
Quench cracking and distortion are generally considered to occur under united thermal and transformational stresses. In this paper quench residual stresses were examined by using a S 55 C steel bar. Various polyalkylene glycol (PAG) solutions and oil were prepared for the quench cooling solutions. The micro structure of the test piece was observed with a metallurgical microscope. The residual stresses caused by quenching were measured by Sachs' method. Considerable tensile and compressive stresses existed on the surface and in the center of the steel. The distribution of stresses and the hardness were related to the PAG content and could be explained clearly by the quench cooling rate.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 53 (487), 475-482, 1987
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679455929600
-
- NII論文ID
- 110002377212
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3133545
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可