Effects of Stress Ratio on Surface- and Interior-Originating Fatigue Properties of High Strength Steel
-
- SHIINA Takahiro
- Division of Mechanical Science, Hokkaido University
-
- NAKAMURA Takashi
- Division of Mechanical Science, Hokkaido University
-
- NOGUCHI Toru
- Division of Mechanical Science, Hokkaido University
Bibliographic Information
- Other Title
-
- 高強度鋼の表面および内部起点型疲労特性に及ぼす応力比の影響
- コウキョウド コウ ノ ヒョウメン オヨビ ナイブ キテンガタ ヒロウ トクセイ ニ オヨボス オウリョクヒ ノ エイキョウ
Search this article
Description
In order to clarify effects of stress ratios (R=σmin/σmax) on surface- and interior-originating fatigue properties, uniaxial fatigue tests of high strength steel (SNCM 439) were carried out under three different stress ratios, R=0.3, 0.1 and -1. Based on tests results and fractographic analysis in initial crack propagation regions (Optically Dark Area (ODA) and Stage 2 a), the following results were obtained, (1) Surface-originating fractures occurred in the same fatigue life region regardless of the stress ratio. On the other hand, interior-originating fractures occurred at a longer fatigue life region, as the stress ratio increased. It is unsure to apply the modified Goodman diagram to high strength steels of which main fracture mode was the interior-originating fracture. (2) In initial crack propagation regions, the fracture surface of the interior-originating fracture was strongly affected by the stress ratio, even though that of the surface-originating fracture was scarcely affected. The formation of a fine bumpy pattern which was characteristic of the ODA's fracture surface was affected by a multiplier effect of the inner environment of material and the compression load.
Journal
-
- TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
-
TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A 70 (696), 1042-1049, 2004
The Japan Society of Mechanical Engineers
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282679456150272
-
- NII Article ID
- 110004998797
-
- NII Book ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
- http://id.crossref.org/issn/03875008
-
- NDL BIB ID
- 7077050
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed