- Preparation of Ni/SiO2 catalyst by chemical fume thermal deposition.
- フンム ネツ ブンカイホウ ニ ヨル Ni SiO2 ショクバイ ノ チョウセ
この論文をさがす
説明
Ni/SiO2 catalysts were prepared by chemical fume thermal deposition. This preparation proceeded as follows. Nickel-salt/methanol solution was sprayed into a tubular reactor with vaporized SiCl4 and air, and then the mixture was immediately pyrolyzed in a reactor whose temperature was controlled at 1573 K at the hottest point.<BR>The apparent diameter of the catalyst produced was estimated by the BET method, and the diameter of NiO, dNiO, x, was measured by XRD. The relationship between dNiO, x and the relative viscosity of sprayed solution, η, was represented by the following equation under the present experimental conditions.<BR>dNiO, x=k (η0.45) n<BR>where n and k are different for each case; n=1.48, k=19 nm for the [Ni (NO3) 2 /CH3OH+air+SiCl4] system, n=1.48, k=32 nm for the [NiCl2 /CH3 OH + air + SiCl4] system, n=0.64, and k=110 nm both for the [Ni (NO3) 2 CH3OH+air] system and the [NiCl2/ CH3OH+air] system.<BR>The apparent growth rate of the catalyst, γap, is proportional to the molar fraction of Ni salt, χ.<BR>γap=kapχ<BR>The reactivity of the catalyst was examined by the methanation of carbon mono-xide as a model reaction. The results show that the activity (TOF) was one or two magnitudes higher than those of conventionally prepared impregnated catalysts.
収録刊行物
-
- 化学工学論文集
-
化学工学論文集 15 (2), 349-356, 1989
公益社団法人 化学工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679487330816
-
- NII論文ID
- 130000870422
-
- NII書誌ID
- AN00037234
-
- ISSN
- 13499203
- 0386216X
-
- NDL書誌ID
- 3220528
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可