- Morphological Change of Antimony Trioxide Fine Particles through Impaction, Compaction or Grinding.
- ショウトツ アッシュク フンサイ ニ トモナウ 3サンカ 2 アンチモン リュ
この論文をさがす
説明
The morphological changes of particles through three different processes (impaction, compaction and grinding) were investigated experimentally. This was done using two types of antimony trioxide (Sb2O3)-fine particles which have almost the same particle size distributions but different surface properties. One has the sulfate group (-SO4) on the surface; the other does not.<br>It is found that the diameter of the Sb2O3 particles having -SO4 begins to increase at lower impaction velocity or at lower compaction pressure than those having no -SO4 does. Estimation of the load applied on a single particle through these two processes reveals that the threshold of the load inducing the particle enlargement is almost the same for impaction and compaction.<br>The tendency for the diameter to change through grinding is opposite to that through impaction or compaction. However, the Sb2O3 particles having -SO4 keep higher crystallinity than those having no -SO4 among these three processes.
収録刊行物
-
- 粉体工学会誌
-
粉体工学会誌 32 (1), 23-30, 1995
一般社団法人 粉体工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679488229376
-
- NII論文ID
- 130003952171
- 40004190010
-
- NII書誌ID
- AN00222757
-
- COI
- 1:CAS:528:DyaK2MXktVWisb8%3D
-
- ISSN
- 18837239
- 03866157
-
- NDL書誌ID
- 3600062
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可