Co-Cr-Pt film with high perpendicular magnetic anisotropy
-
- KEITOKU Toshiaki
- AIT(Akita Research Institute of Advanced Technology)
-
- ARIAKE Jun
- AIT(Akita Research Institute of Advanced Technology)
-
- HONDA Naoki
- AIT(Akita Research Institute of Advanced Technology)
-
- OUCHI Kazuhiro
- AIT(Akita Research Institute of Advanced Technology)
Bibliographic Information
- Other Title
-
- 高垂直磁気異方性Co-Cr-Pt薄膜
- コウスイチョク ジキ イホウセイ Co Cr Pt ハクマク
Search this article
Abstract
Magnetic properties of Co-Cr-Pt thin films for perpendicular magnetic recording media were studied in terms of film composition. Relatively high perpendicular coercivity(Hc_<⊥>) greater than 5000 Oe was obtained at 13-18 at% Cr content and 14-21 at% Pt content. Perpendicular squareness (SQ_<⊥>) and the maximum absolute value of the nucleation field (H_N) were equal to unity and 2500 Oe, respectively. Magnetic anisotropy field (Hk) greater than 10 kOe for Co-Cr-Pt films also was obtained for both Cr and Pt contents of 12-24 at%, preferably for reducing thermal relaxation and medium noise of future high density recording.
Journal
-
- ITE Technical Report
-
ITE Technical Report 24.32 (0), 25-30, 2000
The Institute of Image Information and Television Engineers
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679500397312
-
- NII Article ID
- 110003687800
-
- NII Book ID
- AN1059086X
-
- ISSN
- 24241970
- 13426893
-
- NDL BIB ID
- 5430845
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- CiNii Articles
-
- Abstract License Flag
- Disallowed