書誌事項
- タイトル別名
-
- Factor of Hetero Space Charge Generation in XLPE under DC Electric Field of 20kV/mm
- 20kV mm テイド ノ チョクリュウ カデンカ ニ オケル カキョウ ポリ
この論文をさがす
説明
This report deals with the mechanism of space charge accumulation in cross-linked polyethylene (XLPE) under DC electric field. Space charge was measured by the pulsed-electroacoustic method with applying DC stress of 20kV/mm. A large amount of hetero space charge accumulated in fresh XLPE sample. Factors to influence the space charge accumulation were analyzed in regard to cross-linking by-product and antioxidant. No space charge was seen when the fresh sample was degassed to remove cross-linking by-products. Introducing acetophenone, one of the cross-linking by-products, in the degassed sample brings no space charge, suggesting that acetophenone itself could not be the direct factor of space charge formation. However, heating this sample up to 150°C brings hetero space charge as were seen in the fresh sample. It is concluded that the hetero space charge may be formed when impurities such as antioxidant dissociate thermally with the help of acetophenone and that the dissociate species are attracted towards both electrodes under DC field to form the hetero space charge.
収録刊行物
-
- 電気学会論文誌． Ａ
-
電気学会論文誌． Ａ 117 (9), 915-921, 1997
一般社団法人 電気学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679577080704
-
- NII論文ID
- 130006839903
- 10007452386
- 10002822716
-
- NII書誌ID
- AN10136312
-
- ISSN
- 13475533
- 03854205
- http://id.crossref.org/issn/13418939
-
- NDL書誌ID
- 4284283
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可