固体高分子形燃料電池のフラッディングにおよぼす触媒層とガス拡散層の劣化の影響

DOI Web Site Web Site 参考文献18件

書誌事項

タイトル別名
  • Influence of Degradations of Catalyst Layer and Gas Diffusion Layer on Flooding in PEFC
  • コタイ コウブンシケイ ネンリョウ デンチ ノ フラッディング ニ オヨボス ショクバイソウ ト ガス カクサンソウ ノ レッカ ノ エイキョウ

この論文をさがす

説明

Regarding a polymer electrolyte fuel cell (PEFC), the influence of degradations of a catalyst layer and a gas diffusion layer which are parts of membrane electrode assembly (MEA) on electrode flooding was investigated. On a PEFC, high humidity operation is desired for high performance because it is necessary to contain much water in proton exchange membrane and ionomer at catalyst layer. Additionally, high gas utilization is required for high system efficiency. However, under these conditions, significant degradation in a cell performance is caused by water-flooding of electrodes. The purpose of this study is to investigate how the degradation of a catalyst layer and a gas diffusion layer give the influence to occur flooding on electrode. The single cell was generated at 0.3A/cm2 under high humidity operation for 10000 hours. And the cell performance was evaluated as cell voltage, cell resistance, IV curves, gas crossover rate, electrochemical surface area and Oxygen gain in order to find which part of the cell dominates such cell degradation. Consequently, it is found that the gas diffusivity degradation finally dominates the decay of the cell performance and it is mainly caused not in the gas diffusion layer but in the catalyst layer.

収録刊行物

参考文献 (18)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ