結晶成長方位および金属組成制御によるY123溶融凝固バルクの超伝導特性の改善

書誌事項

タイトル別名
  • Improved Superconducting Properties of Y123 Melt-solidified Bulks through Controlling Crystal Growth Direction and Cation Stoichiometry
  • ケッショウ セイチョウ ホウイ オヨビ キンゾク ソセイ セイギョ ニ ヨル Y123 ヨウユウ ギョウコ バルク ノ チョウデンドウ トクセイ ノ カイゼン

この論文をさがす

抄録

Two new approaches to fabricate Y123 melt-solidified bulks with excellent superconducting properties have been developed. One is a new method of crystal growth from a seed crystal with its c-axis parallel to the top surface, and the other is a high-temperature annealing process under a moderately reducing atmosphere after crystal growth. In the present study, the former method increased the area of high-Jc regions, and the latter enhanced Jc, particularly at positions far from the seed crystal at low temperatures through suppression of yttrium substitution for barium. The field-trapping property was also improved through introduction of a reductive annealing process prior to oxygen annealing at low temperatures.

収録刊行物

  • 低温工学

    低温工学 46 (3), 125-130, 2011

    公益社団法人 低温工学・超電導学会 (旧 社団法人 低温工学協会)

参考文献 (16)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ