書誌事項
- タイトル別名
-
- Microstructures and High Temperature Properties of Ni3Al with B and/or Hf.
抄録
An intermetallic compound, Ni3Al shows an unusual property that strength increases with higher temperature in the range below 900°C.<br>Accordingly, it seems to be applicable to turbine blades for jet engines. However, it is well known that the hot workability is markedly inferior.<br>From these viewpoints, the effects of a small amount of B and Hf on hot workability, microstructures, and high temperature strengths were investigated.<br>The specimens used in this experiment contained about 11% Al and indicated duplex structures of γ and nearly 30% γ′. Therefore, they showed on reverse dependence on temperature with regard to high temperature strength.<br>Adequately added B and Hf to the specimens improved creep rupture strength at 750 and 800°C and hot workability.
収録刊行物
-
- 圧力技術
-
圧力技術 37 (1), 19-26, 1999
一般社団法人 日本高圧力技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679593155968
-
- NII論文ID
- 130004092100
-
- ISSN
- 13479598
- 03870154
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可