- Fatigue Fracture Mechanism Maps for SUS304 Stainless Steel
- SUS304 ステンレス コウ ノ ヒロウ ハカイ キコウ リョウイキズ
この論文をさがす
説明
Fatigue fracture mechanism maps at room temperature and 300°C for SUS304 stainless steel were established by SEM observation of the fracture surface. Depending on the crack propagation rate ranging from 1x10-11 m⁄cycle to 1x10-6 m⁄cycle, three types of fracture surfaces were observed. One was crystallographic fracture region which was flat and dark by SEM observation, second was featureless fracture region which was rough and white, and third was striation region which was typical fatigue failure. Fraction of these regions in fracture surface depends on the crack propagation rate, so the fatigue fracture mechanism maps are useful for the fractography of the fatigue failure accidents.
収録刊行物
-
- 圧力技術
-
圧力技術 41 (5), 216-223, 2003
一般社団法人 日本高圧力技術協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679593173376
-
- NII論文ID
- 130004446708
- 10011799070
-
- NII書誌ID
- AN00011762
-
- ISSN
- 13479598
- 03870154
-
- NDL書誌ID
- 6721223
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可