- KASAI Naoya
- Graduate School of Environment and Information Sciences, Yokohama National University
-
- SEKINE Kazuyoshi
- Graduate School of Environment and Information Sciences, Yokohama National University
-
- KATOH Kimiyasu
- Graduate student, Yokohama National University
書誌事項
- タイトル別名
-
- The detection of fatigue damage accumulation and hydrogen embrittlement in 7075 alloy by the eddy current method
- detection of fatigue damage accumulation and hydrogen embrittlement in 7075 alloy by the eddy current method
この論文をさがす
抄録
In this study, the detection of fatigue damage accumulation and hydrogen embrittlement in 7075 alloy was confirmed using the eddy current method. Fatigue damage and hydrogen charging were accumulated in notched specimens, and then changes in amplitude and phase were measured in the specimens using eddy current testing. The maximum values of the signals were observed at an area where fatigue damage and hydrogen charging were accumulated. The experimental results correlated with accumulation of fatigue damage and hydrogen charging in the specimens. Therefore, the possibility of using this method for the quantitative evaluation of fatigue damage accumulation and hydrogen embrittlement in aluminum alloys is presented.
収録刊行物
-
- 圧力技術
-
圧力技術 44 (5), 256-262, 2006
一般社団法人 日本高圧力技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679593339648
-
- NII論文ID
- 10018300901
-
- NII書誌ID
- AN00011762
-
- ISSN
- 13479598
- 03870154
-
- NDL書誌ID
- 8533769
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可