- Ultra-High-Cycle Fatigue Properties and Evaluation of Crack Growth Life of Dual Phase Stainless Steels
- 2ソウ ステンレス コウ ノ チョウコウサイクル ヒロウ トクセイ ト キレツ シンテン ジュミョウ ヒョウカ
この論文をさがす
説明
This report shows results of fatigue properties and fracture mechanism of dual phase stainless steels. The dual phase stainless steels are often used because of advantageous properties of corrosion resistance for seawater, weldability and workability. Recently, a new fatigue problem becomes important, because number of cycles to failure that should be taken into consideration for maintenance increases over 107. For the ultra-high-cycle fatigue, interior inclusions in materials are dominant factor in fatigue life, but the fracture mechanism is not made clear completely. <br> Results of the ultra-high-cycle fatigue properties are shown. The interior fracture takes place at ultra-high-cycle region. The crack growth life is predicted by using fracture mechanics.
収録刊行物
-
- 圧力技術
-
圧力技術 43 (3), 146-150, 2005
一般社団法人 日本高圧力技術協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679594775936
-
- NII論文ID
- 10015678331
-
- NII書誌ID
- AN00011762
-
- ISSN
- 13479598
- 03870154
-
- NDL書誌ID
- 7390862
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可