Crack Growth Behavior and Redistribution of Residual Stress Caused by Crack Propagation from Residual Tensile Stress Field through Residual Compressive Stress Field

DOI Web Site 10 References

Bibliographic Information

Other Title
  • 引張残留応力場から圧縮残留応力場にき裂が伝播する場合の溶接残留応力の再配分とき裂進展挙動
  • ヒッパリ ザンリュウ オウリョクバ カラ アッシュク ザンリュウ オウリョクバ ニ キレツ ガ デンパ スル バアイ ノ ヨウセツ ザンリュウ オウリョク ノ サイハイブン ト キレツ シンテン キョドウ

Search this article

Abstract

Crack Growth Behavior and Redistribution of Residual Stress Caused by Crack Propagation from Residual Tensile Stress Field through Residual Compressive Stress Field of stress corrosion cracking (SCC) and Fatigue. At the beginning, re-distribution of Residual Stress Field boiled and depended on crack propagation was clarified. Based on analysis output, the crack propagation examination check by fatigue test was done. Comparison analyses of analysis output and a fatigue testing result were performed, and consideration was added.