- Improvement of CAI Strength and Its Mechanisms on CFRTP Laminate with Thinning in Ply-thicknes
- ハクソウカ ニ ヨル CFRTP セキソウバン ノ CAI キョウド コウジョウ ト ソノ メカニズム
この論文をさがす
抄録
In this paper, the effect of thinning in ply-thickness on improvement of compression after impact (CAI) strength and the mechanisms in carbon fiber reinforced thermoplastics (CFRTP) was investigated. This improvement with thinning in ply-thickness was achieved by reduction of growth of fiber/matrix debondings inside each ply to transverse crack. Higher fracture toughness of matrix resin itself was also expected to contribute arresting the crack growth. By combining thinning in ply-thickness and higher fracture toughness of matrix, internal impact damage in CFRTP was dramatically suppressed. Two kinds of CFRTP laminates, in which one had 40 μm ply-thickness and the other had 120 μm ply-thickness, were prepared in order to observe the difference of morphology in internal impact damage and to evaluate the relation between CAI strength and projected impact damage area. Here, thickness of the both laminates was 3 mm. The projected impact damage area was measured with ultrasonic inspection. The effect of ply-thickness on initiation and propagation of internal impact damage, such as fiber/matrix debonding, delamination, and transverse crack, was discussed based on detailed cross-sectional observation of these internal damage with optical and laser microscope. In this study, polyamide 6 was used as matrix resin of CFRTP. Impact energy applied to CFRTP laminates was 1.5 J/mm.
収録刊行物
-
- 日本複合材料学会誌
-
日本複合材料学会誌 39 (3), 89-98, 2013
一般社団法人 日本複合材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679598294912
-
- NII論文ID
- 10031170972
-
- NII書誌ID
- AN00196748
-
- COI
- 1:CAS:528:DC%2BC3sXhsV2qs7%2FN
-
- ISSN
- 18848559
- 03852563
-
- NDL書誌ID
- 024655108
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可