Influence of air-abrasion and subsequent heat treatment on bonding between zirconia framework material and indirect composites

DOI IR IR (HANDLE) Web Site PubMed 6 Citations 40 References
  • SHIMOE Saiji
    Department of Anatomy and Functional Restorations, Division of Oral Health Sciences, Hiroshima University Graduate School of Biomedical Sciences
  • TANOUE Naomi
    Division of General Dentistry, Nagasaki University Hospital
  • KUSANO Kenta
    Department of Anatomy and Functional Restorations, Division of Oral Health Sciences, Hiroshima University Graduate School of Biomedical Sciences
  • OKAZAKI Masayuki
    Department of Biomaterials Science, Division of Molecular Medical Science, Hiroshima University Graduate School of Biomedical Sciences
  • SATODA Takahiro
    Department of Anatomy and Functional Restorations, Division of Oral Health Sciences, Hiroshima University Graduate School of Biomedical Sciences

Search this article

Description

The purpose of this study was to evaluate the influence of air-abrasion and subsequent heat treatment on the shear bond strength of the bond between indirect composites and a zirconia material. Four surface preparations were employed; ground flat, then heated to regenerate the crystal phase (C); air-abraded with alumina for 10 s (S10), for 20 s (S20), and air-abraded for 10 s and heated (H). Disks were primed with Alloy Primer and bonded either with Estenia or with Gradia composite. XRD analysis suggested that the monoclinic zirconia content was increased by air-abrasion, and decreased by heating. The surface roughness of S10, S20 and H disks was similar. Nevertheless, H groups showed lower bond strengths than the S10 and S20 groups both before and after thermal cycling. Although alumina air-abrasion considerably enhanced bonding between zirconia and indirect composites, subsequent heat treatment had a negative effect on the durability of bond strength.

Journal

  • Dental Materials Journal

    Dental Materials Journal 31 (5), 751-757, 2012

    The Japanese Society for Dental Materials and Devices

Citations (6)*help

See more

References(40)*help

See more

Related Projects

See more

Keywords

Details 詳細情報について

Report a problem

Back to top