Influence of Heat Input and Pre-Weld Heat Treatment Condition on Properties of Maraging Steel Weldments.
-
- EL-BATAHGY Abdel-Monem
- Welding Metallurgy Laboratory, Central Metallurgical R & D Institute
書誌事項
- タイトル別名
-
- Influence of Heat Input and Pre-Weld He
この論文をさがす
抄録
This study is focused on the dependence of microstructure and mechanical properties of maraging steel welded joints on both heat input and pre-weld heat treatment condition. Two different procedures were used for producing fully heat treated welded joints. Procedure I included solution annealing before welding then, aging after welding. Procedure II included full heat treatment (solution annealing and aging) before welding then, aging after welding.<BR>It is found that optimizing heat input decreased austenite content and prevented coarsening of weld metal dendritic structure, HAZ grain size and grain boundary precipitates which in turn prevented softening of welded joints.<BR>Restoring properties in the HAZ and developing good strength in the weld metal are depended on pre-weld heat treatment condition. Optimum combination of tensile strength, elongation, toughness and structure of welded joints are attained using procedure I. This is due to forming of homogeneous microstructure consisting of fine weld metal dendrites, fine martensite and fine intermetallic compounds in addition to less retained austenite.<BR>However, satisfactory welded joints can be obtained using procedure II which should be applied in the case of manufacturing large-size welded assemblies since only the welding zone are treated locally after assembly.
収録刊行物
-
- 溶接学会論文集
-
溶接学会論文集 15 (4), 574-583, 1997
一般社団法人 溶接学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679700062080
-
- NII論文ID
- 130003934471
- 110003421830
-
- NII書誌ID
- AN1005067X
-
- ISSN
- 24348252
- 02884771
-
- NDL書誌ID
- 4354441
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可