Heat-resisting Brazing of Stainless Steel SUS316L with Newly Developed Palladium Containing Filler Metals(Report 2). Heat-resisting Brazing of Stainless Steel SUS316L with Palladium-Nickel Based Filler Metals.

DOI 1 Citations

Bibliographic Information

Other Title
  • 新開発パラジウムろうによるステンレス鋼ＳＵＳ３１６Ｌの耐熱ろう付　（第２報）　Ｐｄ‐Ｎｉ系パラジウムろうによるステンレス鋼ＳＵＳ３１６Ｌの耐熱ろう付
  • Heat-resisting Brazing of Stainless Steel SUS316L with Newly Developed Palladium Containing Filler Metals (Report 2)
  • 新開発パラジウムろうによるステンレス鋼SUS316Lの耐熱ろう付(第2報)

Search this article

Description

This paper summarized metallurgical and mechanical properties of stainless steel SUS316L joints brazed with two types of newly deve10ped palladium-nickel based filler metals, 40Pd-5ONi-10Co, 30Pd -50Ni-10Cu-10Co, commercial palladium containing filler metal, 33Pd-64Ag-3Mn(BPd-10), and nickle-based filler metal, Ni-Co-Cr-Mo-Fe-B.<BR>The main results obtained were as follows:<BR>(1) The maximum joint strengths at room temperature were the joints brazed with the palladium-nickel based filler metal 40Pd-5ONi-10Co and 30Pd-5ONi-10Cu-10Co, then the mean values were 516 MPa.<BR>(2) The 30Pd-5ONi-10Cu-10Co filler metal showed the highest joint strength at 873 K or below, and the 33Pd-64Ag-3Mn filler metal showed the highest joint strength at 1073 K.<BR>(3) Joints brazed with 40Pd-5ONi-10Co and 30Pd-5ONi-10Cu-10Co have superlor creep rupture resistance at 673 K and 873 K, and the brazed joints with Ni-Co-Cr-Mo-Fe-B offered longer rupture time at 1073 K than those with palladium-nickel base filler matals.<BR>(4) The 30Pd-50Ni-10Cu-10Co filler metal is the best filler metal for heat-resisting brazing.

Journal

Citations (1)*help

See more

Keywords

Details 詳細情報について

  • CRID
    1390282679700689920
  • NII Article ID
    130003934268
  • DOI
    10.2207/qjjws.11.43
  • COI
    1:CAS:528:DyaK3sXksFensbw%3D
  • ISSN
    24348252
    02884771
    http://id.crossref.org/issn/02884771
  • Text Lang
    ja
  • Data Source
    • JaLC
    • Crossref
    • CiNii Articles
  • Abstract License Flag
    Disallowed

Report a problem

Back to top