Thinning Behavior of the Spinline in High-Speed Bicomponent Spinning of High Molecular Weight and Low Molecular Weight Poly(ethylene terephthalate).
-
- Radhakrishnan J.
- Department of Organic and Polymeric Materials, Tokyo Institute of Technology
-
- Kikutani Takeshi
- Department of Organic and Polymeric Materials, Tokyo Institute of Technology
-
- Okui Norimasa
- Department of Organic and Polymeric Materials, Tokyo Institute of Technology
書誌事項
- タイトル別名
-
- Thinning Behavior of the Spinline in Hi
この論文をさがす
説明
The high-speed spinning of sheath/core type bicomponent fibers consisting of high molecular weight poly(ethylene terephthalate) (HMPET) and low molecular weight poly(ethylene terephthalate) (LMPET) was performed and the thinning behavior of the spinline was investigated. At lower speeds, the on-line measurement of the spinline diameter revealed that the diameter profile of the bicomponent spinning lies in between those of the HMPET and LMPET single component spinnings. At higher speeds, a neck-like doformation was also found to occur in the bicomponent spinnings. The position of the neck-like deformation was closer to the spinneret in comparison with both the single component spinnings. Although the necklike deformation occurred in the bicomponent spinning, the LMPET component in the bicomponent fiber showed low oriented and low crystalline structure.
収録刊行物
-
- 繊維学会誌
-
繊維学会誌 52 (11), 618-622, 1996
社団法人 繊維学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679805068928
-
- NII論文ID
- 10001798748
-
- NII書誌ID
- AN00131651
-
- ISSN
- 18842259
- 00379875
-
- NDL書誌ID
- 4077843
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可