The Influence of Chain Entanglement Density on the Increase in Strength and Modulus with Ultra-drawing of Ultra-high-molecular-weight Polypropylene

DOI Web Site Web Site 参考文献17件 オープンアクセス

書誌事項

タイトル別名
  • The Influence of Chain Entanglement Density on the Increases in Strength and Modulus with Ultra-drawing of Ultra-high-molecular-weight Polypropylene.
  • Influence of Chain Entanglement Density on the Increase in Strength and Modulus with Ultra drawing of Ultra high molecular weight Polypropylene

この論文をさがす

説明

The influence of chain entanglement density on the ultra-drawing of ultra-high-molecular-weight polypropylene (UHMW-PP) has been studied by comparison of the gel-like spherulite pressing method (the GSP method) and the gel-casting method, using two kinds of specimens prepared from 2.0wt% solution of UHMW-PP. The only major difference between the specimens in both methods is the cooling rate of solution. The influence of chain entanglement density in an undrawn specimen on the increase in strength and modulus with ultra-drawing has been discussed. It was found that the slopes of strength and modulus versus draw ratio (DR) were steeper in the gel-casting method. This difference was concluded to be due to the difference of chain entanglement density of undrawn specimens, by considering the fine structure and the maximum draw ratio (λmax). And, it was considered that the differences in the above slopes between both methods could not be explained by the changes of crystalline orientation and crystalline size but by the change of fraction of folded-chain crystals (or extended-chain crystals) with ultra-drawing.

収録刊行物

  • 繊維学会誌

    繊維学会誌 58 (12), 444-450, 2002

    社団法人 繊維学会

参考文献 (17)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ