綿セルロース布の弱酸性あるいは中性条件下でのTEMPO触媒酸化

DOI Web Site Web Site 被引用文献4件

書誌事項

タイトル別名
  • TEMPO‐Mediated Oxidation of Cotton Cellulose Fabrics under Weakly Acidic or Neutral Conditions
  • ワタ セルロースフ ノ ジャクサンセイ アルイハ チュウセイ ジョウケン カ デ ノ TEMPO ショクバイ サンカ

この論文をさがす

抄録

Cotton fabrics were oxidized with TEMPO/NaClO/NaClO2 or 4‐acetamido‐TEMPO/NaClO/NaClO2 system in water at pH 3.8 or 6.8 and 40-80℃ for 0-120 min. As references, cotton fabrics were oxidized with TEMPO/NaBr/NaClO system in water at pH 10 and room temperature for 0-45 min. In all cases, the higher the carboxylate content of the oxidized cotton fabric, the lower its viscosity‐average degree of polymerization (DPv). However, the oxidation at pH 3.8 and 6.8 gave cotton fabrics with higher DPv values at carboxylate contents > 0.3 mmol/g, compared to those prepared at pH 10. When the cotton fabrics oxidized with 4‐acetamido‐TEMPO/NaClO/NaClO2 system in water at pH 3.8 or 6.8 were heated at 105℃ for 2 h, clear whiteness reductions were observed, a part of which may have been caused by thermal degradation of 4‐acetamido‐TEMPO‐related compounds physically adsorbing on the oxidized cotton fabrics and slightly remaining in them even after repeated washing with water. When ethylene glycol, gluconic acid or glucose was directly added to the aqueous solution containing the cotton fabric after the oxidation, the oxidized cotton fabrics had relatively low whiteness reduction and low bending resistance (or better softness for clothes) even after heating at 105℃ for 2 h. Thus, the TEMPO‐ or 4‐acetamido‐TEMPO‐mediated oxidation in water at pH 3.8 or 6.8 may be applicable to chemical modification of cotton fabrics to be used as clothes for functionalized underwear.

収録刊行物

  • 繊維学会誌

    繊維学会誌 71 (5), 191-196, 2015

    社団法人 繊維学会

被引用文献 (4)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ