Color stability, gloss, and surface roughness of indirect composite resins
-
- Jain Vishal
- Division of Dental Biomaterials, Indiana University School of Dentistry
-
- A. Platt Jeffrey
- Division of Dental Biomaterials, Indiana University School of Dentistry
-
- Moore Keith
- Division of Dental Biomaterials, Indiana University School of Dentistry
-
- M. Spohr Ana
- Department of Dental Materials, Pontifical Catholic University of Rio Grande do Sul
-
- A. Borges Gilberto
- Department of Restorative Dentistry, University of Uberaba
この論文をさがす
説明
This in vitro study evaluated the color stability, gloss, and surface roughness (Ra) of four indirect composites. Enamel and dentin shades of Radica, Sculpture Plus, Belleglass-NG, and Gradia Indirect were evaluated for color stability. Specimens were stored in a staining solution (coffee) and assessed every 3 days for a period of 21 days, after which color difference (∆E*) was calculated. Only enamel shades were used for measuring gloss and surface roughness at 0, 5000, 10,000, and 20,000 cycles of simulated toothbrushing. The results were statistically analyzed using repeated measures analysis of variance (ANOVA) and Tukey’s test. Statistically significant changes in ∆E* during the 21-day period were observed in all indirect composites for enamel and dentin shades, and ∆E* was greater than the clinically acceptable value of 3.3. Belleglass-NG showed the least change in ∆E*, while Sculpture Plus had large changes in ∆E*. In all groups, gloss was 75% lower than baseline values after 10,000 cycles of toothbrushing. After 20,000 cycles, surface roughness was highest in Radica and lowest in Belleglass-NG. Belleglass-NG had higher color stability and gloss retention, and lower surface roughness, as compared with the other composite systems. (J Oral Sci 55, 9-15, 2013)