リサイクル原料から固相合成させたフェライトを担持した陶磁器質材料
書誌事項
- タイトル別名
-
- Pottery Materials Containing Solid-Phase Synthesized Ferrite from Recycled Raw Materials.
- リサイクル ゲンリョウ カラ コアイアイ ナサセタ フェライト オ タンジ シタ トウジキシツ ザイリョウ
この論文をさがす
説明
Recently, there has been a strong interest in recycling technologies for industrial waste. In this study, pottery materials containing Mn-Zn ferrite were manufactured by solid-phase reaction sintering, using grinding sludge from bearings and recycled powder from dry-cell batteries. Evaluation of the materials characteristics, confirmed that Mn-Zn ferrite was generated in fired products. The ferrite content was higher after reduced atmosphere firing than after oxidized atmosphere firing, and increased as the firing temperature rose. The electromagnetic wave absorption characteristics of the fired products had practical efficiency at 1180°C and 1200°C reduced atmosphere firing, but had low efficiency at 1160°C reduced atmosphere firing and 1200°C oxidized atmosphere firing.
収録刊行物
-
- 日本応用磁気学会誌
-
日本応用磁気学会誌 26 (11), 1125-1130, 2002
公益社団法人 日本磁気学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680068195200
-
- NII論文ID
- 110002809501
- 130004478748
-
- NII書誌ID
- AN0031390X
-
- ISSN
- 18804004
- 02850192
-
- NDL書誌ID
- 6341842
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- NDLデジコレ（旧NII-ELS）
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可