大気中反応焼成によるSr‐Zn‐W型フェライト粉末の磁気特性ならびにボンド磁石の作製
書誌事項
- タイトル別名
-
- Magnetic Properties of Sr-Zn-W-Type Ferrite Powders Prepared by Reaction Sintering in Air and Production of Bonded Magnets
- 大気中反応焼成によるSr-Zn-W型フェライト粉末の磁気特性ならびにボンド磁石の作製
- タイキ チュウ ハンノウ ショウセイ ニ ヨル Sr Zn Wガタ フェライト フンマツ ノ ジキ トクセイ ナラビニ ボンド ジシャク ノ サクセイ
この論文をさがす
抄録
An experiment was carried out to improve the magnetic properties of Sr-Zn-W-type hexagonal ferrite powders, and bonded magnets were prepared from these powders. It was found that W-type hexagonal ferrite is easily producible in the air by replacing the Fe2+ part with Zn2+. The preparation conditions for a typical sample were as follows; chemical composition: SrO·1.5ZnO·0.5FeO·8Fe2O3 with added 0.3 wt% SiO2, 0.7 wt% CaO, 1.0 wt% SrCO3; reaction sintering condition: 1300°C × 4.0 h in air; annealing condition: 1050°C × 5 min in air. The magnetic properties of Sr-Zn-W-type hexagonal ferrite powder are σs=92.9 × 10-6Wb·m/kg, HcJ=187.8 kA/m. The magnetic properties of hybrid (mixed 80% M-type ferrite powder and 20% W-type ferrite powder) bonded magnets are Br=295 mT, (BH)max=16.6 kJ/m3, HcJ=177 kA/m.
収録刊行物
-
- 日本応用磁気学会誌
-
日本応用磁気学会誌 29 (4), 436-441, 2005
公益社団法人 日本磁気学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680068375808
-
- NII論文ID
- 110002811814
-
- NII書誌ID
- AN0031390X
-
- ISSN
- 18804004
- 02850192
-
- NDL書誌ID
- 7305590
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- NDL-Digital
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可