- Ru underlayer effect on the Fe-Si magnetic film
- Fe Si ジセイ マク ニ オヨボス Ru シタジソウ ノ コウカ
この論文をさがす
抄録
The Fe-Si magnetic film with an Ru underlayer was fabricated and characterized. In the film, the Fe-Si grain became small when using a very thin Ru underlayer. In addition, the surface roughness of Fe-Si film with a thin Ru underlayer became smaller than that without an Ru underlayer. Consequently, the hard axis coercivity of the Fe-Si film with a 1 nm Ru underlayer was about 1.1 Oe, which was much lower than that of the same film without an Ru underlayer. The Fe-Si film with a 1 nm Ru underlayer had a clear uniaxial magnetic anisotropy (anisotropy field Hk: 18 Oe), a hard axis relative permeability of 900, and a ferromagnetic resonance (FMR) at around 1.6 GHz. A very sharp peak of the imaginary part of permeability μh" was observed at the FMR frequency. This was due to the clear uniaxial magnetic anisotropy and small anisotropy dispersion.
収録刊行物
-
- 日本応用磁気学会誌
-
日本応用磁気学会誌 29 (8), 826-830, 2005
公益社団法人 日本磁気学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680068794880
-
- NII論文ID
- 110002811842
- 130004478974
-
- NII書誌ID
- AN0031390X
-
- COI
- 1:CAS:528:DC%2BD2MXpsFChtL4%3D
-
- ISSN
- 18804004
- 02850192
-
- NDL書誌ID
- 7436747
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- NDL-Digital
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可