    • PERPENDICULAR MAGNETIC ANISOTROPY AND MAGNETO-OPTICAL SPECTRA OF MBE GROWN MnPt3/Co MULTILAYERS

    DOI 被引用文献1件 参考文献9件 オープンアクセス

    書誌事項

    公開日
    1998
    DOI
    • 10.3379/jmsjmag.22.s2_85
    公開者
    公益社団法人 日本磁気学会

    この論文をさがす

    説明

    MnPt3/Co multilayer films were grown by the molecular-beam epitaxy (MBE) onto MgO(111) substrates at a temperature of 300 °C. Small angle XRD measurements demonstrated that the samples had multilayered structure with sharp MnPt3/Co interfaces. The appearance of superlattice lines due to Cu3Au structure confirmed a partial formation of the ordered phase in the MnPt3 layers. The [MnPt3(1.9 nm)/Co(0.4 nm)]20 multilayer showed a preferential magnetization perpendicular to the film plane and a 100% perpendicular remanence. The Kerr spectrum of the multilayer had a negative peak of -0.24 deg around 1.4 eV and showed a enhancement in the high energy region. This result implies the existence of the ordered phase in the MnPt3 layer and alloying layer of Co and Pt at the MnPt3/Co interface.

    収録刊行物

    被引用文献 (1)*注記

    もっと見る

    参考文献 (9)*注記

    もっと見る

    キーワード

    詳細情報 詳細情報について

    • CRID
      1390282680069871872
    • NII論文ID
      130004925676
    • DOI
      10.3379/jmsjmag.22.s2_85
    • ISSN
      18804004
      02850192
    • 本文言語コード
      en
    • データソース種別
      • JaLC
      • Crossref
      • CiNii Articles
      • OpenAIRE
    • 抄録ライセンスフラグ
      使用不可

    問題の指摘

    ページトップへ