- Microscopic Observation of Inclusions Related to Microstructure Evolution in Low Carbon Steel Ti-B Weld Metal
- Ti-B系低炭素鋼溶接金属の組織形成に関与した介在物の微視的観察
- Ti Bケイ テイタンソコウ ヨウセツ キンゾク ノ ソシキ ケイセイ ニ カンヨシタ カイザイブツ ノ ビシテキ カンサツ
この論文をさがす
抄録
Microstructures of low carbon submerged arc weld metals of a Ti–B system with different aluminum contents were analyzed. The inclusions contributing to formation of acicular ferrite were directly sliced into thin foils and crystallographic analyses were performed.<br>In the sample with low Al/O ratio (0.48–0.73), acicular ferrite microstructure was observed. Meanwhile, bainite microstructure was observed in the specimen with an Al/O ratio of 1.52. The inclusions contributing to formation of acicular ferrite were surrounded by a narrow Ti-enriched zone which was analyzed as TiO. The Baker–Nutting orientation relationship was satisfied between the TiO and acicular ferrite. It was supposed that the TiO on the inclusion surface contributes to the heterogeneous nucleation of acicular ferrite supplying low interface energy.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 95 (1), 65-70, 2009
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680102648320
-
- NII論文ID
- 110007008526
-
- NII書誌ID
- AN10528571
-
- ISSN
- 1341688X
- 18832954
- 00211575
- http://id.crossref.org/issn/00211575
-
- COI
- 1:CAS:528:DC%2BD1MXos1Cnsg%3D%3D
-
- NDL書誌ID
- 9766506
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可