Analysis of Peritectic Reaction in Ag-18 mass%Sn Alloy
-
- Hattori Yuhi
- Department of Materials Science and Engineering, National Defense Academy
-
- Esaka Hisao
- Department of Materials Science and Engineering, National Defense Academy
-
- Shinozuka Kei
- Department of Materials Science and Engineering, National Defense Academy
Bibliographic Information
- Other Title
-
- Ag-18 mass%Sn合金における包晶反応過程の解析
- Ag-18 mass%Sn ゴウキン ニ オケル ホウショウハンノウ カテイ ノ カイセキ
Search this article
Abstract
In order to investigate the peritectic reaction, Ag-18 mass%Sn alloy has been used in this study. Approximately 10 g of this alloy was melted in the alumina crucible. Using a fine K-type thermocouple, thermal history during cooling was recorded. The peritectic reaction was observed at about 725 ºC, which corresponded to the equilibrium phase diagram. The metallographic SEM observation of the specimen, which was quenched at 725 ºC, revealed that the secondary phase, ζ phase, completely covered the primary (Ag) phase. These indicated that ζ phase easily nucleated on the primary (Ag) phase and the peritectic reaction rapidly finished. EBSD analysis showed that plural crystals of ζ phase covered on the single crystal of (Ag) phase. This also indicated that ζ phase formed easily on the (Ag) phase. The analysis of relation between temperature and phase fraction indicated that thick ζ phase rapidly formed along the (Ag) phase / liquid interface and peritectic reaction plays a major part of transformation in this alloy system formed in an isothermal cooling.
Journal
-
- Tetsu-to-Hagane
-
Tetsu-to-Hagane 102 (7), 380-388, 2016
The Iron and Steel Institute of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282680102752768
-
- NII Article ID
- 130005159405
-
- NII Book ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL BIB ID
- 027505482
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed