- Composition and Corrosion Behavior of Hot-dip Al-Si-Mg Alloy Coated Steel Sheets
- ヨウユウ Al-Si-Mg ゴウキンメッキ コウバン ノ メッキ ソセイ ト フショク キョドウ
この論文をさがす
抄録
This study was intended to investigate the effect of the amount of Mg and Si addition in the Al-Si coating in order to improve corrosion resistance of Aluminized steel sheets.<br> A salt spray test using formed specimens proved that Al-8mass%Si-6mass%Mg-coated steel sheet having less cracks in the alloy layer after forming has the best corrosion resistance.<br> This outdoor exposure test using unformed specimens for 10 years proved that corrosion weight loss of Al-8mass%Si-6mass%Mg-coated steel sheet was reduced to approximately 30% less than that of Aluminized steel sheets and approximately 70% less than that of 55% aluminum-zinc alloy-coated steel sheets; thereby, it was possible to confirm that Al-8mass%Si-6mass%Mg-coated steel sheet has favorable corrosion resistance under a long-term atmospheric environment.<br> This is supported to be the protective effects caused by corrosion products mixed with Si and Mg, since the current value of the cathode polarization method of the specimen of Al-8mass%Si-6mass%Mg-coated steel sheet after the outdoor exposure test in an artificial rain solution were reduced by approximately 40% less than that of aluminized steel sheet.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 99 (10), 617-624, 2013
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680102937728
-
- NII論文ID
- 130004540867
-
- NII書誌ID
- AN10528571
-
- ISSN
- 1341688X
- 18832954
- 00211575
-
- COI
- 1:CAS:528:DC%2BC3sXhs1CgsrzJ
-
- NDL書誌ID
- 024921804
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可