- Low Temper Embrittlement and Brittle-to-ductile Transition in 0.2 mass% Carbon Steels
- 0.2 mass%炭素鋼における低温焼戻し脆性と脆性-延性遷移挙動
- 0.2 mass%タンソコウ ニ オケル テイオン ヤキモドシゼイセイ ト ゼイセイ-エンセイ センイ キョドウ
この論文をさがす
抄録
Low temperature temper embrittlement of low carbon steels was investigated. 0.2 mass % carbon steels with fully martensitic structure were employed. The specimen was tempered at 473 K, 623 K and 873 K for 7.2 ks. Impact absorbed energy tested at room temperature shows the lowest value for the specimen tempered at 623 K while the value of Vickers hardness decreases with the increasing in the temperature tempered. Temperature dependence of impact absorbed energy was also measured, exhibiting the brittle-to-ductile transition temperature was highest in the specimen tempered at 623 K, which is low temperature temper embrittlement. Inter-granular fracture was observed in the specimens tempered at 623 K and 873 K, which indicates that tempering at not less than 623 K tends to increase the BDT temperature due to the inter-granular fracture. The temperature dependence of yield stress was also measured, showing that the athermal stress in the specimen tempered at 873 K was drastically decreased, which tends to decrease the BDT temperature. These opposite temperature dependences against BDT temperature induce the low temper embrittlment.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 102 (6), 340-346, 2016
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680103561088
-
- NII論文ID
- 130005154147
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 027443483
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可