熱間せん断加工後焼き入れした切り口における水素脆化耐性

DOI DOI Web Site Web Site Web Site 被引用文献10件 参考文献10件 オープンアクセス

書誌事項

タイトル別名
  • Resistance of Hydrogen Embrittlement on Hot-Sheared Surface during Die-Quench Process
  • ネツカン セン ダンカコウ ゴ ヤキ イレ シタ キリクチ ニ オケル スイソゼイカ タイセイ

この論文をさがす

説明

This study investigated resistance of hydrogen embrittlement on a hot-sheared surface of die-quenched steel sheets. The specimens were sheared at 750 °C and 650 °C after austenitization, and then quenched by water cooling. Additionally, the specimens were cathodically hydrogenized for 48 hours to accelerate cracking by hydrogen embrittlement. This sequence resulted in the residual tensile stress of over 1 GPa on the sheared surface and hydrogen concentration of about 1.5 ppm. Despite these severe conditions, cracking by hydrogen embrittlement was not observed. The state of micro-structure in the vicinity of the sheared surface might cause this high resistance against cracking. Indeed, sub-micron grained ferrite or deformed uncertain soft and hard phases, which might be more ductile than martensite, were observed around the sheared surface.

収録刊行物

  • 鉄と鋼

    鉄と鋼 100 (3), 359-365, 2014

    一般社団法人 日本鉄鋼協会

被引用文献 (10)*注記

もっと見る

参考文献 (10)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ