鋳鉄に及ぼすカルシウム・ハイドライド添加の影響

DOI Web Site Web Site

書誌事項

タイトル別名
  • THE EFFECTS OF CALUCIUM HYDRIDE ADDITION TO GREY CAST IRON
  • チュウテツ ニ オヨボス カルシウム ハイドライド テンカ ノ エイキョウ

この論文をさがす

抄録

The authors studied the effects of calcium hydride addition to grey cast iron and the following results were obtained: <BR>1) Spheroidal graphite cast iron could be obtained by addition of calucium hydride (CaH2) in excess of 4% to a suitable molten iron (Swedish charcoal pig iron) covered with the flux of fluorspar. <BR>2) When CaH2 and fluspar were added without any other additions, it was difficul to give all spheroidal graphite structure, and always quasi-flake graphite was distributed in it. <BR>3) More spongy blow holes occurred with higher addition of CaH2 and fluospar, but when the spheroidal graphite structures occurred, most of the blow holes disappeared. <BR>4) For suitable iron (Swedish charcoal pig iron), the addition of both 2% CaH2 and Mgalloy was not so effective to decrease the amount of Mg which was necessary to make spheroidal graphite. <BR>5) For the pig iron seemed to be oxidized, when blow holes appeared by addition of CaH2, spheroidalization of graphite might occur by the same amount of additional Mg as to Swedish charcoal pig iron. <BR>6) The effect of desulphurization was observed by addition of the CaH2 spread over the molten iron.

収録刊行物

  • 鉄と鋼

    鉄と鋼 42 (4), 338-343, 1956

    一般社団法人 日本鉄鋼協会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ