高Ｃｒフェライト系耐熱鋼の組織，逆Ｓ字クリープ破断強度に及ぼすＣｒ，Ａｌ，Ｎｉの影響

Asakura Kentaro, Koseki Toshihiko, Sato Takashi, Arai Masahiko, Horiuchi Toshiaki, Tamura Koji, Fujita Toshio

doi:10.2355/tetsutohagane.96.665

書誌事項

タイトル別名

Effect of Chromium, Aluminum and Nickel on Microstructure and Reverse-S Type Creep Rupture Strength of High Cr Ferritic Heat Resistant Steels
コウCr フェライトケイタイネツコウノソシキギャクSジクリープハダンキョウドニオヨボス Cr Al Ni ノエイキョウ
Effect of Chromium, Aluminum and Nickel on Microstructure and Reverse-S type Creep Rupture Strength of High Cr Ferritic Heat Resisting Steels

この論文をさがす

説明

Microstructure and creep strength of two high-Cr ferritic heat resistant steels –11Cr and 9Cr - were investigated at a temperature of 650°C. 11Cr steel containing relatively higher carbon, aluminum and nickel than 9Cr steel showed a significant drop in creep strength after 1000 h, while 9Cr showed a recovery in creep strength after a slight drop. 11Cr steel contained M₂₃(CB)₆, Z phase and a relatively coarsened Laves phase as precipitates after 7000 h at a temperature of 650°C, while the 9Cr steel contained fine MX, ultrafine M₆C, as well as M₂₃(CB)₆ and Laves phase. Z phase was not found and the growth of Laves phase was retarded in the 9Cr steel. Hence, it was concluded that the drop in creep strength of 11Cr steel was attributed to the coarsened Laves and Z phases, and the recovery of creep strength in the 9Cr steel to the fine MX and M₆C precipitates. The experimental results on the effect of steel composition on the stability of precipitates in steels were thermodynamically consistent with the Thermo-Calc calculation results, which used an existing database. We concluded that chromium and aluminum increased the kinetics of the formation and coarsening of the precipitates.

収録刊行物

ＩＳＩＪ　Ｉｎｔｅｒｎａｔｉｏｎａｌ

ＩＳＩＪ　Ｉｎｔｅｒｎａｔｉｏｎａｌ 52 (5), 902-909, 2012

一般社団法人日本鉄鋼協会

キーワード

詳細情報詳細情報について

書き出し

問題の指摘