SUS 304における粒界クリープ損傷とクリープ特性

DOI Web Site Web Site 被引用文献6件 参考文献6件

書誌事項

タイトル別名
  • Creep-induced Grain Boundary Damage and Creep Properties of SUS 304
  • SUS304 ニ オケル リュウカイ クリープ ソンショウ ト クリープ トク

この論文をさがす

抄録

For the purpose of evaluating creep damage, systematic study of creep damage was performed, particularly for grain boundary creep damages by SEM observation and density change measurements. Three different kinds of grain boundary creep damages leading to creep fracture were observed. They are cracks formed at triple points at higher loading stress, grain boundary cavities at medium stress and cracks at sigma/austenite interface at lower stress. Both the grain boundary cavities and the cracks at sigma/austenite interface comence to form at comparatively low creep strain (0.1-0.6%) at the steady-state creep stage (t/tr:0.2-0.4).The increasing feature of cavity volume with creep time corresponds to the creep curves. Precipitation of AIN associated with sigma phase on grain boundary leads to early formation of the cracks at their interface. In this case, the volume of the cracks increases considerably in the accelerating creep stage and constitutes a main component of the creep strain. The rapid increase in the volume causes the transition from the steady-state to the accelerating creep stage.

収録刊行物

  • 鉄と鋼

    鉄と鋼 74 (10), 2009-2016, 1988

    一般社団法人 日本鉄鋼協会

被引用文献 (6)*注記

もっと見る

参考文献 (6)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ