高温鋼板のスプレ冷却に関する研究

DOI Web Site Web Site 被引用文献6件 参考文献5件

書誌事項

タイトル別名
  • Study on the Water Spray Cooling of Steel Plate at High Tempeature
  • コウオン コウハン ノ スプレ レイキャク ニ カンスル ケンキュウ

この論文をさがす

説明

The cooling process of plain carbon steel plate was studied. A plate of 28 × 220 × 220 mms size was heated up to 930°C and then cooled by water spray from both sides; the temperature of cooling water was 38°C. The results obtained are as follows;<BR>1. The heat transfer coefficient α' decreases gradually as the temperature of cooled surface θsis raised when water flow rate of spray W is large, while in the case whereWis small, the coefficient decreases abruptly with the elevation of θsover 300°C.<BR>2. The relation between α′ and W is described as “α′∝Wn” in the case of W>5 × 10-4 1/cm.2rnin, and values of n are divided into two groups according to the boiling condition of cooling water, i. e.groups of value having 03-0.5 and0.5-0.8<BR>3. The relation between the mean heat transfer coefficient and W is described as “α∝W0.65-0.75” in the case of W>5 × 10-41/cm2.min.<BR>4. The relation between a and cooling water temperature θW(°C) is described as “α∝ [1-(5-8)×10-3θw]” in the case of W=0.060-%-0.062 1/crn2.min.<BR>5. When W is large, the cooling rate V is hardly influenced by Os, but increases abruptly for 0, lower than about 500°C when W is small. Furthermore, V' decreases regardless of W, in such a temperature region that the transformation heat is evolved.<BR>6. The relation between the mean cooling rate V- andWis described as “vcx 1470.-0.7” in the case of W=5 ×10-4-8 × 10-2 l/cm2-min.<BR>7. The relation between V and θw(°C) is described as “V∝ [1 (4.5-5.5)× 10-3θw]” in the case of W=0.060-0.062l/cm2.min.<BR>8. It is deduced that “spray cooling is a sort of turbulent flow cooling” from the quantitative relation between the water flow rate of spray W and heat transfer coefficient a, i. e.“α∝Wn” where values ofnis about0.5-0.8.

収録刊行物

  • 鉄と鋼

    鉄と鋼 54 (14), 1457-1471, 1968

    一般社団法人 日本鉄鋼協会

被引用文献 (6)*注記

もっと見る

参考文献 (5)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ