- Properties of Cold and Hot Pressed Briquets Made of Reduced Ore Powder
- フンジョウ カンゲンコウ オ モチイタ レイカン オヨビ ネッカン セイケイ
この論文をさがす
抄録
The rednced ore powder for sample was prepared by reducing Hamersley hematite ore with pressurized hydrogen gas at about 900°C in a pilot plant for fluidized bed reduction. The cold and hot pressed briquets were produced from the meduced ore powder using a die at various temperatures.<BR>The influences of compacting load at various temperatures On the crushing strength, density, and rate of reoxidation with a mixture of oxygen and nitrogen gas at 250°C to 800°C were investigated.<BR>The following results were obtained.<BR>1) To obtain the briquets of high crushing strength and high density, it was desirable to use reduced ore powder above the reduction degree of about 90%.<BR>2) The maxinum rate of reoxidation of briquets was observed at about 400°C, and the reason for this became evident.<BR>3) Hot pressing at 500°C tO 600°C under lower compacting load than that of cold pressing was effective for obtaining high crushing strength of briquets.<BR>4) The reoxidation rate of briquets was controlled by a parabolic law and decreased with increased density of briquets.<BR>5) Sintering of briquets at temperatures of 800°C to 1100°C for 4hrs was not effective for the increase in density.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 65 (10), 1517-1525, 1979
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680130879872
-
- NII論文ID
- 110001487850
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 2063674
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可