- Toughness of High Manganese-Chromium Austenitic Steels at Liquid Helium Temperature
- コウ Mn Cr オーステナイト コウ ノ エキタイ ヘリウム オンド ニ オ
この論文をさがす
抄録
In order to examine the applicability of high manganese-chromium austenitic steels to cryogenic use, Charpy impact test was made at liquid helium temperature. A steel with 25Mn-5Cr-1Ni as base composition exhibited good toughness in impact testing without any sign of martensite transformation induced by impact deformation.<BR>Niobium bearing steel, which was grain-refined, showed slightly lower impact energy. The cause for this was considered to be the local strain hardening in fine-grained steel, in which the mode of crack propagation was changed. Increment of nickel content to the material with base composition increased toughness. 15Mn-5Cr-5Ni steel exhibited good toughness even though the trace of martensite transformation caused by low stability of austenite was found. As the results above, it was shown that 25Mn-5Cr-1Ni austenitic steels have an applicability to cryogenic use.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 65 (6), 681-686, 1979
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680131246080
-
- NII論文ID
- 110001487951
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 2052116
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可