Ni-Cr-W系およびNi-Cr-W-Mo系合金の組織と高温強度

DOI Web Site Web Site 参考文献5件

書誌事項

タイトル別名
  • Microstructure and Creep Rupture Strength of Ni-Cr-W and Ni-Cr-W-Mo Alloys
  • Ni Cr Wケイ オヨビ Ni Cr W Moケイ ゴウキン ノ ソシキ ト

この論文をさがす

抄録

To obtain the basic knowledge needed for the development of alloys used for heat exchanger which is operated at near 1000°C in the nuclear steel making process, microstructure and creep rupture strength of Ni-Cr-W and Ni-Cr-W-Mo alloys which contain 12-20%Cr, 0-35%W and 0-25%Mo at 1000°C, have been investigated.<BR>The results are summerized as follows:<BR>(1) Solubility limit of Cr and W in Ni-Cr-W system is shown as Cr+ W≅39 (wt%). Above this limit of content of chromium plus tungsten, α-W is observed as second phase. When Mo is added to Ni-Cr-W alloy, Win the second phase, α-W, is gradually substituted by Ni, Mo and finally the second phase changes to μ-phase.<BR>(2) Creep strength of Ni-Cr-W solid solution alloy increases with increasing W content. The high creep strength is presumarably attributed to decrease of diffusion rate with increasing W content. The substitution of W by Mo decreases the creep strength.<BR>(3) Metallic phase α-W increases the creep and creep rupture strength. Intermetallic compound μ, however, increases creep strength, but does not increase creep rupture strength. This is caused by the preferential nucleation of cracks on the interface between matrix and μ-phase.

収録刊行物

  • 鉄と鋼

    鉄と鋼 65 (7), 1031-1040, 1979

    一般社団法人 日本鉄鋼協会

参考文献 (5)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ