We measured the micro-Vickers hardness of 0.26 %-carbon steel, which had been subjected to rotatory bending stress at a high temperature. The fatigue test was conducted at the room temperature, 300°C and 550°C mainly, and hardness testing was held under 1000 gram load. Summary of the results is as follows : (l) At 300°C, the increase of the hardness number is greater and the hardening layer is deeper than that at the room temperature. But at 550°C, the hardness change is little or nothing. (2) Moreover, this hardening layer is caused by the repeated stress above about 0.8 σω at the room temperature, but about 0.65 σω at 300°C, where σω is the endurance limit at each temperature.
収録刊行物
-
- 日本機械学會論文集
-
日本機械学會論文集 26 (161), 86-90, 1960
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680132172288
-
- NII論文ID
- 110002351093
-
- NII書誌ID
- AN00187419
-
- ISSN
- 21859485
- 00290270
-
- NDL書誌ID
- 9150493
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可