Cantilever beam type rotating fatigue test was conducted at the temperatures of room temperature, 300°C and 500°C at a frequency of 10 000 rpm, and as the check test, same type fatigue test was carried out at room temperature at the frequency of 2 450 rpm. The material used here was 0.26% carbon steel. Specimens tested were three types of different stress concentration factors; ακ=1.0, ακ=1.8 and ακ=3.0 (these values are Neuber's calculation). The following is the summarized conclusion of the experimenta1 results. In the high frequency fatigue, the sharper the notch, the more decreasing the fatigue strength; as the notch is sharper, the fatigue notch factor has larger value than that of the stress concentration factor, especially at elevated temperatures.
収録刊行物
-
- 日本機械学會論文集
-
日本機械学會論文集 29 (206), 1632-1639, 1963
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680134526464
-
- NII論文ID
- 110002351941
- 110002442864
-
- NII書誌ID
- AN00187419
-
- ISSN
- 21859485
- 24242675
- 00290270
-
- NDL書誌ID
- 9151253
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可