- Thermal Crack in the Carbide Face-Milling Cutter : 2nd Report, Its Significance as a Cause of Tool Failures
- チョウコウショウメン フライス ニ オケル アツキ レツ 2
この論文をさがす
抄録
Several sorts of cracks which appear in the carbide face-milling cutter, including the thermal crack, are investigated in respect with their significances as the causes of tool failures which occur over a wide range of the cutting speed. Tool failures at a high cutting speed are classified into several types from their appearances and each type concerns with a singular crack. The so-called thermal crack is one of these cracks which cause the tool failures at a high cutting speed. The cutting speed, the feed and the cutting fluid influence the sort of the crack which causes the tool failure so that the type of the failure changes. Including the thermal crack, some cracks are explainable that they are due to the fatigue of the carbide at an elevated temperature. But there are a few of such cracks that do not conform to the above mentioned explanation.
収録刊行物
-
- 日本機械学會論文集
-
日本機械学會論文集 28 (193), 1055-1066, 1962
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680135296384
-
- NII論文ID
- 110002351668
-
- NII書誌ID
- AN00187419
-
- ISSN
- 21859485
- 00290270
-
- NDL書誌ID
- 9151021
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可