書誌事項
- タイトル別名
-
- Effect of Cold Working and High Temperature Treatment of High Carbon Chromium Bearing Steel on Its Rolling Contact Fatigue Life
- ジクウケ コウ ノ ジュミョウ ニ オヨボス レイカン アツエン ト コウオン
この論文をさがす
抄録
High-carbon chromium bearing steel tubes rolled in the cold pilger mill were tested in the thrust type rolling contact fatigue testing machine. Their fatigue lives were evaluated as influenced by cold rolling and also by spheroidization at high temperature heat treatment of sulfides elongated during cold rolling. Life of cold rolled tubes with a regular 70% of reduction in area extended more than three times as long as that of hollows and the same cold rolled ones endured over six times more than hollows when heat treated as high temperatures subsequent to cold rolling. It was revealed that nonmetallic inclusions finely dispersed by cold rolling and sulfides spheroidized by high temperature treatment as well contributed to a remarkable improvement in fatigue life of high-carbon chromium bearing steel.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 70 (8), 854-860, 1984
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680158593536
-
- NII論文ID
- 110001495219
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 2985772
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可