18-8ステンレス鋼の耐孔食性に及ぼす鋼中SおよびMn量の影響

DOI Web Site Web Site 被引用文献4件 参考文献6件 オープンアクセス

書誌事項

タイトル別名
  • Effects of S and Mn Contents on Pitting Resistance of 18-8 Stainless Steel
  • 18 8 ステンレス コウ ノ タイ コウショクセイ ニ オヨボス コウチュウ
公開日
1984
DOI
  • 10.2355/tetsutohagane1955.70.7_741
公開者
一般社団法人 日本鉄鋼協会

この論文をさがす

説明

The effects of S and Mn contents on pitting corrosion behavior of 18-8 stainless steel have been studied by means of anodic polarization and immersion test in chloride media. The main results obtained are summarized as follows:<BR>In 3% NaCl solution at 0 and 30°C, pitting potential (V'c100) had tendency to become less noble with the increase in S content. This tendency, however, could not be found for the specimens containing S above about 0.01%. On the other hand, V'c100 continuously became less noble with the increase in Mn content. In 3% NaCl solution at 70°C or 3% NaCl acidic (HGl) solution at 30°C, V'c100 depended on S and Mn contents, and it became noble with the decrease in those elements. In 10% FeCl3·6H2O solution at 25°C, the frequency of occurrence or the density of pits increased with the increase of the quantity of sulfide inclusions. On the other hand, the growth tendency of pits depended on the Mn/S ratio, and anodic reaction of specimen was retarded with decrease of the ratio. In all of the specimens, the pit initiation site, was sulfide inclusion/metal interface in the pitting potential region in NaCl and FeCl3·6H2O solution, and pit grew preferentially into the metal matrix.

収録刊行物

  • 鉄と鋼

    鉄と鋼 70 (7), 741-748, 1984

    一般社団法人 日本鉄鋼協会

被引用文献 (4)*注記

もっと見る

参考文献 (6)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ