The Simple Determination Method of Precipitates in Steels by X-ray Diffraction Technique with Y2O3 as Internal Standard Materials

CHINO Atsushi, ISHIBASHI Youichi, GUNJI Naoki, IWATA Hideo

doi:10.2355/tetsutohagane1955.77.11_2027

Bibliographic Information

Other Title

Y2O3内標準X線回折法による鋼中析出物の簡易定量法
Y2O3内標準X線回折法による鋼中析出物の簡易定量法
Y2O3 ナイヒョウジュン Xセンカイセツホウニヨルコウチュウセキシ

Search this article

Description

The simply quantitative state analysis method of precipitates in steels has been established by X-ray diffraction technique with adding constant amount of Y₂O₃ as internal standard material. The procedure is as follows : (1)The residues extracted from steels by potentiostatic electrolysis are dispersed in methanol with 100 ml beaker. (2)5.0 ml of Y₂O₃ dispersing solution (50 mg/250 ml methanol) is added in above mentioned solution and after that this solution is dispersed by ultrasonic vibration. (3)This solution is filtrated and the residues are collected on filter. (4)The X-ray diffraction pattern of residues is measured and its peak intensity ratios of precipitates to Y₂O₃ are calculated. The amount of precipitates are determined from these peak intensity ratios by calibration curves, which are preliminaly made from relation between peak intensity ratio and the amount of precipitates. This method can simply estimate state of precipitates quantitatively compared with conventional extracted residues decomposition method.

Journal

Tetsu-to-Hagane

Tetsu-to-Hagane 77 (11), 2027-2032, 1991

The Iron and Steel Institute of Japan

Keywords

Details 詳細情報について

Export

Report a problem

The Simple Determination Method of Precipitates in Steels by X-ray Diffraction Technique with Y<SUB>2</SUB>O<SUB>3</SUB> as Internal Standard Materials