合金化溶融亜鉛めっき鋼板の金属間化合物コーティング層のクラックと基材鋼の結晶粒界の関係

DOI HANDLE Web Site Web Site 被引用文献3件 参考文献17件 オープンアクセス

書誌事項

タイトル別名
  • Relation between Cracking of Intermetallic Coating Layer of Galvannealed Steel Sheet and Grain Boundary of Substrate Steel
  • ゴウキンカ ヨウユウ アエンメッキ コウハン ノ キンゾク カン カゴウブツ コーティングソウ ノ クラック ト キザイ コウ ノ ケッショウ リュウカイ ノ カンケイ

この論文をさがす

説明

Multiple cracking behavior and its relation to the grain boundary of the substrate steel were investigated. The crack spacing and its distribution of the specimens strained to prescribed strains were observed with a scanning electron microscope. The crystallographic orientation of the substrate grains was estimated from the electron back scattering pattern. The images of the cracks of the coating layer and grain boundaries of the substrate steel were combined together with image processing software to know whether the cracking of coating layer initiates above the substrate grain boundaries or not. The main results are summarized as follows. (1) The cracking of the coating layer initiates in the regions just above the substrate grain boundaries. (2) The cracks that initiate above the substrate grain boundaries propagate transversely; namely they propagate into the region, below which no substrate grain boundary exists. (3) It was suggested the cracking of the coating layer initiates above the small angle grain boundaries or above the grain boundaries intact to the grains with large Schmid factors. (4) In the multiple cracking process of the coating layer, the similarity of the crack spacing distribution to the grain boundary spacing distribution is kept.

収録刊行物

  • 鉄と鋼

    鉄と鋼 91 (3), 342-348, 2005

    一般社団法人 日本鉄鋼協会

被引用文献 (3)*注記

もっと見る

参考文献 (17)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ