10Cr-2Mo-V-Nb耐熱鋼のクリープ破断強さと微細組織におよぼすCr量変化の影響

DOI Web Site Web Site 被引用文献1件

書誌事項

タイトル別名
  • Effect of Chromium on Creep Rupture Strength and Microstructure of 10Cr-2Mo-V-Nb Heat Resisting Steel
  • 10Cr 2Mo V Nb タイネツ コウ ノ クリープ ハダン ツヨサ ト

この論文をさがす

抄録

The effect of chromium content on high temperature properties of ferritic heat resisting steel containing Mo, V and Nb was studied. The amount of chromium content was varied from 3% to 15% in order to obtain the optimum value. The tempering hardness and tensile strength were measured and the creep rupture tests were carried out in the temperature range from 550°C to 700°C. The microstructure was observed by transmission electron microscope.<BR>The results indicated that the low chromium steels had a good tempering resistance in shorter term tempering, but had a tendency to soften remarkably after longer term tempering. As increasing the chromium content up to 8%, the tensile strength increased but the ductility decreased. It was observed in transmission electron microscopy that the coalescence of precipitates was accelerated, but the recovery of matrix was markedly retarded with increase in chromium content.<BR>It was concluded that the optimum chromium content obtained from creep rupture tests and so on, was 10% at the temperature of 600°C.

収録刊行物

  • 鉄と鋼

    鉄と鋼 66 (9), 1375-1384, 1980

    一般社団法人 日本鉄鋼協会

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ