Failure Analysis of Seamless Line Pipe during Transportation by Ship
-
- YAGI Akira
- Yawata R & D Lab., NipPon Steel Corp.
-
- NISHIDA Shin-ichi
- Yawata R & D Lab., NipPon Steel Corp.
-
- HIGASHIYAMA Hirokichi
- Yawata R & D Lab., NipPon Steel Corp.
-
- URASHIMA Chikayuki
- Yawata R & D Lab., NipPon Steel Corp.
-
- KAJIKI Etsuharu
- Yawata Works,Now Tokyo Works,Nippon Steel Corp.
-
- OKADA Hideki
- Yawata Works, NipPon Steel Corp., Now Reed Nippon Corp.
Bibliographic Information
- Other Title
-
- 船積輸送したシームレス鋼管の損傷解析
- フナズミ ユソウシタ シームレス コウカン ノ ソンショウ カイセキ
Search this article
Abstract
Break out had happened during field hydraulic test of unused line pipe. The observation of failure pipe indicated presence of the pre-damage at the broken portion. We supposed that the damage would have occurred during manufacturing or shipping. From analysis offracture surface and failure section, follow ing facts were revealed<BR>(1) The cracks propagate in wall thickness direction independently of the metal-flow of hot rolling direction.<BR>(2) The crack initiation sites are the external and the internal surfaces of the pipe and the cracks propagate stepwise with smooth fracture surface.<BR>(3) In the fracture surface, many corrosion products are observed and clear striations are locally recognized.<BR>It was concluded that the failure was caused by fatigue crack during shipment. This mechanism was confirmed by the pulsating bending fatigue test of pipes.
Journal
-
- Tetsu-to-Hagane
-
Tetsu-to-Hagane 71 (14), 1663-1669, 1985
The Iron and Steel Institute of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282680159524096
-
- NII Article ID
- 110001490947
-
- NII Book ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL BIB ID
- 3039374
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed