塗装鋼板の密着性と塗膜/クロメート化成処理鋼板界面での相互作用の検討

DOI Web Site Web Site 参考文献13件

書誌事項

タイトル別名
  • Adhesion between Paint and Steel Sheet in Paint-coated Steel Sheet System and Interaction at Interface between Paint and Chromate-coated Steel Sheet
  • トソウ コウハン ノ ミッチャクセイ ト トマク クロメート カセイ ショリ コウハン カイメン デ ノ ソウゴ サヨウ ノ ケントウ

この論文をさがす

説明

The interface between paint and chromate-coated steel sheet in the paint-coated steel sheet system were investigated using ATR IR spectroscopy technique to elucidate interactions between the paint and steel sheet. The paint composed of a mixture of alkyd resin and melamine resin, and the steel sheet modified with chromic acid were used as specimens for the experiments. In order to observe IR spectra at the paint/ chromate-coated steel sheet interface, the paint layer coated on the chromate-coated steel sheets was sandpapered to make thin layer of less than 1 μm thickness, which was smaller than the penetration length of Evanescent wave. The paint at the paint/ chromate-coated steel sheet interface showed different IR spectrum from the bulk of the paint layer. C=O absorption (1722 cm-1) in the alkyd resin showed weak intensity, and a new absorption at 1600 cm-1 appeared. Such changes in the IR spectrum indicate that C=O groups in alkyd resin could interact with the steel sheet to contribute to adhesion of the paint/chromate-coated steel sheet adhesive joints.

収録刊行物

  • 鉄と鋼

    鉄と鋼 92 (8), 495-500, 2006

    一般社団法人 日本鉄鋼協会

参考文献 (13)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ